| 产地/厂家:LG化学 | 类型:标准料 |
供应耐高温ABS/LG化学/XR-407E
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 融体流动速率 | 200℃/5kg | ASTM D-1238 | 1 | g/10min |
| 融体流动速率 | 220℃/10kg | ASTM D-1238 | 7 | g/10min |
| 熔体流动速率 | 230℃/3.8kg | ASTM D-1238 | 3 | g/10min |
| 比重 | ASTM D-792 | 1.08 | g/cc | |
| 模具收缩率 | ASTM D-955 | 0.4-0.7 | % | |
| 拉伸屈服强度 | 50mm/min | ASTM D-638 | 450 | kg/cm2 |
| 拉伸模量 | 1mm/min | ASTM D-638 | 23000 | kg/cm2 |
| 屈服伸长率 | 50mm/min | ASTM D-638 | 6 | % |
| 断裂伸长率 | 50mm/min | ASTM D-638 | 20 | % |
| 弯曲强度 | 15mm/min | ASTM D-790 | 750 | kg/cm2 |
| 弯曲模量 | 15mm/min | ASTM D-790 | 25500 | kg/cm2 |
| IZOD缺口冲击强度 | 1/4" 23℃ | ASTM D-256 | 18 | kg.cm/cm |
| IZOD缺口冲击强度 | 1/4" -30℃ | ASTM D-256 | 8 | kg.cm/cm |
| IZOD缺口冲击强度 | 1/8" 23℃ | ASTM D-256 | 19 | kg.cm/cm |
| IZOD缺口冲击强度 | 1/8" -30℃ | ASTM D-256 | 8 | kg.cm/cm |
| 洛氏硬度 | ASTM D-785 | 110 | R-scale | |
| 热变形温度 | 18.5kg/cm21/4"退火 | ASTM D-648 | 110 | ℃ |
| 热变形温度 | 18.5kg/cm21/4"未退火 | ASTM D-648 | 105 | ℃ |
| 热变形温度 | 4.6kg/cm21/4" 退火 | ASTM D-648 | 119 | ℃ |
| 热变形温度 | 4.6kg/cm21/4" 未退火 | ASTM D-648 | 114 | ℃ |
| 维卡软化点 | 5kg 50℃/h | ASTM D-1525 | 115 | ℃ |
| 阻燃等级 | 1/8" | UL94 | HB | calss |
| 阻燃等级 | 1/16" | UL94 | HB | calss |
供应商信息
| 企业类型 | 个体工商户 | 注册资本 | 108万人民币 | ||
| 公司注册地址 | 常州市新北区罗溪镇塑化路25-10-105 | 法定代表人 | 邹长锋 | ||
| 公司成立日期 | 2006-6-1 | 经营范围 | ABS/AS/亚克力塑料原料 | ||
产品推荐
推荐产品
本页信息为常州浙东塑料有限公司为您提供的"供应耐高温ABS/LG化学/XR-407E"产品信息,如您想了解更多关于"供应耐高温ABS/LG化学/XR-407E"价格、型号、厂家请联系厂家,或给厂家留言。 进入店铺
在线留言