| 厂家(产地)：伊斯曼化学 | 牌号：0601 | 销售方式：品牌经销 |
| 类型：标准料 | 加工级别：注塑级、 挤出级 | 特性级别：透明级 |
| 用途级别：通用级 |
伊士曼共聚聚酯简介：
共聚聚酯是全新的透明工程塑料系列，高透明度高抗冲性高耐化学性的***组合。透光率达91%，达到有机玻璃的透明，冲击性韧性极好接近甚至超过聚碳酸酯。适合注塑、挤塑、挤吹加工，可应用于化妆品包装、透明文具、透明家电、牙刷、玩具、医疗、吹瓶、薄膜、片材等等透明材料应用的领域。
主要特性：
清澈透明
优良的抗冲击性
高耐化学性
优良的可注塑性
耐高温性
良好的二次加工性
强抗刮花性
符合美国FDA和其它相关认证
安全、环保，不含双酚A
| Product Data Sheet Drystar? 0601 Copolyester | ||
| Application/UsesInjection molding | ||
| Product Description | ||
Eastman is pleased to announce the launch of DRYSTAR* copolyesters. This new product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman s copolyesters are highly valued for their excellent balance of properties such as superior aesthetics, impact strength, and chemical resistance. These properties can be optimally realized when the resins are properly dehydrated in accordance to recommended drying conditions and equipment. Recognizing this value, Eastman conceived Drystar? copolyesters to allow converters with limited access to desiccant dryers to achieve these optimizations. In addition, some converters with desiccant dryers may still find Drystar? copolyesters value-adding to attain production flexibility and cost saving by removing the drying process prior to injection molding, profile extruding, or extrusion blow molding copolyesters. The initial launch comprises of the commercialization of four grades of Drystar? copolyesters and Eastman has on-going program to extend this strategic product-line in the future. *DRYSTAR is only available in the Asia Pacific Region. | ||
| Typical Properties | ||
| Propertya | Testb Method | Typical Value, Unitsc |
| Film Properties | ||
| Inherent Viscosity d (film) | EMN-A-AC-G-V-1 | 0.70 |
| Thickness of Film Tested | D 374 | 250 microns (10 mils) |
| Density | D 1505 | 1.27 g/cm3 |
| Haze | D 1003 | 0.8% |
| Gloss @ 45° | D 2457 | 108 |
| Transparency | D 1746 | 85% |
| Regular Transmittance | D 1003 Modified | 89% |
| Total Transmittance | D 1003 Modified | 91% |
| Water Vapor Transmission Rate e | F 1249 | 7 g/m2· 24h (0.5 g/100in.2· 24h ) |
| Gas Permeability, CO2 | D 1434 | 49 cm3· mm/m2· 24h· atm (125 cm3· mil/100in.2· 24h· atm ) |
| Gas Permeability, O2 | D 3985 | 10 cm3· mm/m2· 24h· atm (25 cm3· mil/100in.2· 24h· atm ) |
| Elmendorf Tear Resistance | ||
| M.D. | D 1922 | 13.7 N (1400 gf) |
| T.D. | D 1922 | 16.7 N (1700 gf) |
| PPT Tear Resistance | ||
| M.D. | D 2582 | 93 N (21 lbf) |
| T.D. | D 2582 | 93 N (21 lbf) |
| Tear Propagation Resistance, Split Tear Method | ||
| @ 254 mm/min (10 in./min) M.D. | D 1938 | 36 N/mm (205 lbf/in.) |
| @ 254 mm/min (10 in./min) T.D. | D 1938 | 36 N/mm (205 lbf/in.) |
| Tear Resistance, Trouser @ 200 mm/min | ||
| M.D. | *** 6383-1 | 36 N/mm (205 lbf/in.) |
| T.D. | *** 6383-1 | 36 N/mm (205 lbf/in.) |
| Tensile Strength @ Yield | ||
| M.D. | D 882 | 52 MPa (7500 psi) |
| T.D. | D 882 | 52 MPa (7500 psi) |
| Tensile Strength @ Break | ||
| M.D. | D 882 | 59 MPa (8600 psi) |
| T.D. | D 882 | 55 MPa (8000 psi) |
| Elongation @ Yield | ||
| M.D. | D 882 | 4% |
| T.D. | D 882 | 4% |
| Elongation @ Break | ||
| M.D. | D 882 | 400% |
| T.D. | D 882 | 400% |
| Tensile Modulus | ||
| M.D. | D 882 | 1900 MPa (2.8 x 105 psi ) |
| T.D. | D 882 | 1900 MPa (2.8 x 105 psi ) |
| Dart Impact f | ||
| @ 23°C (73°F) | D 1709A Modified | 400 g |
| @ -18°C (0°F) | D 1709A Modified | 500 g |
| Mechanical Properties (Injection Molded), ASTM Method | ||
| Specific Gravity | D 792 | 1.27 |
| Water Absorption, 24 h immersion | D 570 | 0.13% |
| Tensile Stress @ Break | D 638 | 28 MPa (4100 psi) |
| Tensile Stress @ Yield | D 638 | 50 MPa (7300 psi) |
| Elongation @ Break | D 638 | 130% |
| Tensile Modulus | D 638 | 2100 MPa (3.0 x 105 psi ) |
| Flexural Modulus | D 790 | 2100 MPa (3.0 x 105 psi ) |
| Flexural Yield Strength | D 790 | 70 MPa (10200 psi) |
| Rockwell Hardness, R Scale | D 785 | 106 |
| Izod Impact Strength, Notched | ||
| @ 23°C (73°F) | D 256 | 101 J/m (1.9 ft· lbf/in.) |
| @ -40°C (-40°F) | D 256 | 37 J/m (0.7 ft· lbf/in.) |
| Impact Strength, Unnotched g | ||
| @ 23°C (73°F) | D 4812 | NB |
| @ -20°C (-4°F) | D 4812 | NB |
| @ -30°C (-22°F) | D 4812 | NB |
| @ -40°C (-40°F) | D 4812 | NB |
| Impact Resistance (Puncture), Energy @ Max. Load | ||
| 2.5-mm (0.100-in.) Thick Plaques, @ 23°C (73°F) | D 3763 | 28 J (21 ft· lbf) |
| 2.5-mm (0.100-in.) Thick Plaques, @ -40°C (-40°F) | D 3763 | 41 J (30 ft· lbf) |
| 3.2-mm (0.125-in.) Thick Plaques @ 23°C (73°F) | D 3763 | 33 J (24 ft· lbf) |
| 3.2-mm (0.125-in.) Thick Plaques @ -40°C (-40°F) | D 3763 | 50 J (37 ft· lbf) |
| Mechanical Properties (Injection Molded), *** Method | ||
| Density | *** 1183, Method D | 1.27 g/cm3 |
| Water Absorption, 24 h immersion | *** 62 | 0.13% |
| Tensile Stress @ Break | *** 527 | 28 MPa |
| Tensile Stress @ Yield | *** 527 | 50 MPa |
| Elongation @ Break | *** 527 | *** |
| Tensile Modulus | *** 527 | 2100 MPa |
| Flexural Modulus | *** 178 | 2000 MPa |
| Flexural Yield Strength | *** 178 | 68 MPa |
| Rockwell Hardness, R Scale | *** 2039-2 | 109 |
| Izod Impact Strength, Notched, Type 1 Specimen, Type A Notch | ||
| @ 23°C | *** 180 | 6.2 kJ/m2 |
| @ -40°C | *** 180 | 4.2 kJ/m2 |
| Impact Strength, Unnotched, Type 1 Specimen h | ||
| @ 23°C | *** 180 | NB |
| @ -20°C | *** 180 | NB |
| @ -30°C | *** 180 | NB |
| @ -40°C | *** 180 | NB |
| Impact Resistance (Puncture), Energy @ Max. Load i | ||
| 2.5-mm Thick Plaques @ 23°C | *** 6603-2 | 40 J |
| 2.5-mm Thick Plaques @ -40°C | *** 6603-2 | 35 J |
| 3.2-mm Thick Plaques @ 23°C | *** 6603-2 | 44 J |
| 3.2-mm Thick Plaques @ -40°C | *** 6603-2 | 36 J |
| Thermal Properties | ||
| Deflection Temperature | ||
| @ 0.455 MPa (66 psi) | D 648 | 70°C (158°F) |
| @ 1.82 MPa (264 psi) | D 648 | 64°C (147°F) |
| Vicat Softening Temperature | D 1525 | 85°C (185°F) |
| Thermal Conductivity | C 177 | 0.21 W/m· K (1.5 Btu· in./h· ft2· °F ) |
| Glass Transition Temperature (Tg) | DSC | 80°C (176°F) |
| Specific Heat | ||
| @ 60°C (140°F) | DSC | 1.30 kJ/kg· K (0.31 Btu/lb· °F) |
| @ 100°C (212°F) | DSC | 1.76 kJ/kg· K (0.42 Btu/lb· °F) |
| @ 150°C (302°F) | DSC | 1.88 kJ/kg· K (0.45 Btu/lb· °F) |
| @ 200°C (392°F) | DSC | 1.97 kJ/kg· K (0.47 Btu/lb· °F) |
| @ 250°C (482°F) | DSC | 2.05 kJ/kg· K (0.49 Btu/lb· °F) |
| Coefficient of Linear Thermal Expansion j | D 696 | 5.1 x 10-5 /°C (mm/mm· °C) (2.8 x 10-5 /°F (in./in.· °F)) |
| Electrical Properties | ||
| Dielectric Constant | ||
| 1 kHz | D 150 | 2.6 |
| 1 MHz | D 150 | 2.4 |
| Dissipation Factor | ||
| 1 kHz | D 150 | 0.005 |
| 1 MHz | D 150 | 0.02 |
| Arc Resistance | D 495 | 158 sec |
| Volume Resistivity | D 257 | 1015 ohm· cm |
| Surface Resistivity | D 257 | 1016 ohms/square |
| Dielectric Strength, Short Time, 500 V/sec rate-of-rise | D 149 | 16 kV/mm (410 V/mil) |
| Typical Processing Conditions | ||
| Drying Temperature k | 70°C (160°F) | |
| Drying Time k | 6 hrs | |
| Processing Melt Temperature | 250-270°C (480-520°F) | |
| Mold Temperature | 15-40°C (60-100°F) | |
东莞市畅之翔塑胶原料有限公司以珠三角地区为基准，业务辐射全国，现与国内外大型塑胶生产商建立了长期友好的合作关系。 公司主要代理韩国LG、美国伊士曼、杜邦、拜耳、BASF、宝理等公司相关塑胶原料。主营产品为美国伊士曼CA、CAB、CAP、PCTA、PCTG、PETG、 Eastman Tritan婴儿奶瓶 运动水壶专用料，ASA、AE、POE、功能性ABS、汽车用工程塑料PC/ASA、PBT/ABS、PC/ABS、PA/ABS等合金材料。长期现货供应PP、HIPS、LDPE、LLDPE、TPV、TPU、TPEE、POM、PA6、PA66、PA46、PA9T、PA12、PPA、PCT、PPS、LCP、PSU、PEI、COC、PEEK等特殊性工程塑料。 公司以“客户、赢利***、真诚服务、售后到位”为服务理念，以***服务网络、热情的服务态度、严格的服务规范、满意的服务效果为标准。为客户提供一站式解决方案，以满足客户的需要。公司全体员工同心协力，真诚为各界朋友的事业发展共助微薄之力；欢迎新老客户订货垂询.
点击查看>| 企业类型 | 有限责任公司(自然人投资或控股) | 注册资本 | 85.00万人民币 |
| 公司注册地址 | 东莞市樟木头镇塑胶原料市场一期Y栋6号 | 统一社会信用代码 | 914419005778664077 |
| 登记机关 | 东莞市工商行政管理局 | 法定代表人 | 熊赛国 |
| 公司成立日期 | 2011-06-24 | 营业期限 | 长期 |
| 经营范围 | 销售：塑胶原料、塑胶制品、其它化工产品；货物进出口、技术进出口。（依法须批准的项目，经相关部门批准后方可开展经营活动。） | ||
-
￥22.50
-
￥22.00
-
￥25.00
-
￥25.00
-
面议
-
面议
-
面议
-
面议
-
￥23.00
-
￥24.00
-
￥22.00
-
￥18.50