ABS 台湾奇美 PA-757GJ08涂覆级TV液晶显示器外壳/DVD音响外壳
| 性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 |
| 机械性能 | 拉伸强度(引张强度) | | ASTM D638/*** 527 | 405 | kg/cm?(MPa)[Lb/in2] |
| 断裂伸长率 | | ASTM D638/*** 527 | 50 | % |
| 拉伸模量 | | ASTM D638/*** 527 | | kg/cm?(MPa)[Lb/in2] |
| 拉伸屈服伸长率(延伸率) | | ASTM D638/*** 527 | | % |
| 拉伸断裂伸长率(延伸率) | | ASTM D638/*** 527 | | % |
| 弯曲模量(弯曲弹性率) | | ASTM D790/*** 178 | 22938 | kg/cm?(MPa)[Lb/in2] |
| 弯曲强度 | | ASTM D790/*** 178 | 622 | kg/cm?(MPa)[Lb/in2] |
| 洛氏硬度 | | ASTM D785 | | |
| IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/*** 179 | 23 | kg·cm/cm(J/M)ft·lb/in |
| 1/4" -30℃ | ASTM D256/*** 179 | | kg·cm/cm(J/M)ft·lb/in |
| 1/8" 23℃ | ASTM D256/*** 179 | 26 | kg·cm/cm(J/M)ft·lb/in |
| 1/8" -30℃ | ASTM D256/*** 179 | | kg·cm/cm(J/M)ft·lb/in |
| Charpy冲击强度 | 23℃ (缺口) | ASTM D256/*** 179 | | kg·cm/cm(J/M)ft·lb/in |
| -30℃(缺口) | ASTM D256/*** 179 | | kg·cm/cm(J/M)ft·lb/in |
| 23℃(无缺口) | ASTM D256/*** 179 | | kg·cm/cm(J/M)ft·lb/in |
| -30℃(无缺口) | ASTM D256/*** 179 | | kg·cm/cm(J/M)ft·lb/in |
| 物性性能 | 比重(密度) | | ASTM D792/*** 1183 | 1.04 | |
| 成型收缩率 | | ASTM D955 | | % |
| 熔融指数(流动系数) | 200℃/5kg | ASTM D1238/*** 1133 | 2.7 | g/10min |
| 220℃/10kg | ASTM D1238/*** 1133 | | g/10min |
| 吸水率 23℃/24H | | ASTM D570/*** 62 | | % |
| 热性能 | 热变形温度 | 退火 | ASTM D648/*** 75 | 98 | ℃(℉) |
| 未退火 | ASTM D648/*** 75 | 87 | ℃(℉) |
| 维卡软化点 | | ASTM D1525/*** R306 | 105 | ℃(℉) |
| 熔点 | | - | | ℃(℉) |
| 燃烧性(率) | | UL94 | | |
| 线性膨胀系数 | | ASTM D696/*** 11359 | | mm/mm.℃ |
| 加工条件 | 干燥条件 | | | | |
| 加工温度 | 射嘴 | | | ℃ |
| 料筒前段 | | | ℃ |
| 料筒中段 | | | ℃ |
| 料筒后段 | | | ℃ |
| 熔体温度 | | | | ℃ |
| 模具温度 | | | | ℃ |
| 压力 | 注塑压力 | | | Mpa |
| 保压压力 | | | Mpa |
| 背压 | | | Mpa |
| 螺杆转速 | | | | rpm |
| 其他 | 备注 | |
| 颜色 | |
| 特性 | 黑色高光泽级之ABS树脂,具省略涂装、着重环保之特性;流动性佳,易于大尺寸模具充填成形。 |
| 用途 | LCD TV、液晶显示器外壳/DVD音响外壳 |