Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min

64

MPa

ASTM D 638

Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min

5

%

ASTM D 638

Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min

40

%

ASTM D 638

Flexural Stress, yld / 挠曲强度, 屈服 , 2.6 mm/min, 100 mm span

96

MPa

ASTM D 790

Flexural Modulus / 挠曲模量, 2.6 mm/min, 100 mm span

2580

MPa

ASTM D 790

Hardness，Rockwell / 洛氏硬度 R

121

–

ASTM D 785

Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C

453

J/m

ASTM D 256

Instrumented IMPACT Energy @ peak / 仪表控制抗冲击能量 @ 峰值, 23°C

54

J

ASTM D 3763

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50

112

°C

ASTM D 1525

HDT（热变形温度）, 1.82 MPa, 3.2mm, unannealed （未退火）

87

°C

ASTM D 648

HDT（热变形温度）, 0.45 MPa, 6.4 mm, unannealed （未退火）

101

°C

ASTM D 648

HDT（热变形温度）, 1.82 MPa, 6.4 mm, unannealed （未退火）

93

°C

ASTM D 648

CTE（线形膨胀系数）, -30°C to 30°C, flow（流动）

7.2E-05

1/°C

ASTM D 696

CTE（线形膨胀系数）, -30°C to 30°C, xflow（横向）

7.2E-05

1/°C

ASTM D 696

Thermal Conductivity / 导热系数

0.2

W/m-°C

ASTM C 177

Relative Temp Index, Elec / 相对热指数， 电性能

85

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

85

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

85

°C

UL 746B

Specific Gravity / 比重

1.18

–

ASTM D 792

Water Absorption / 吸水率, 24 hours

0.1

%

ASTM D 570

Water Absorption，equilibrium / 吸水率，平衡, 23C

0.4

%

ASTM D 570

Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm

0.4 – 0.6

%

SABIC Method

Mold Shrinkage / 收缩率, xflow（横向）, 3.2 mm

0.4 – 0.6

%

SABIC Method

Melt Flow Rate / 熔流率,, 260°C/2.16 kgf

22

g/10 min

ASTM D 1238

Volume Resistivity / 体积电阻率

1.6E+17

Ohm-cm

ASTM D 257

Surface Resistivity / 表面电阻率

>1.E+16

Ohm

ASTM D 257

Dielectric Strength, in oil / 耐电强度，在油中, 3.2 mm

24.3

kV/mm

ASTM D 149

Relative Permittivity / 相对介电常数, 50/60 Hz

2.8

–

ASTM D 150

Relative Permittivity / 相对介电常数, 1 MHz

2.7

–

ASTM D 150

Dissipation Factor / 耗散因素, 50/60 Hz

0.0052

–

ASTM D 150

Dissipation Factor / 耗散因素, 1 MHz

0.0071

–

ASTM D 150

Arc Resistance, Tungsten / 耐电弧性 {PLC}

6

PLC Code

ASTM D 495

Hot Wire Ignition / 热丝引燃 {PLC)

2

PLC Code

UL 746A

High Voltage Arc Track Rate / 高电压电弧起痕速率 {PLC}

3

PLC Code

UL 746A

High Ampere Arc Ign, surface / 高电流电弧引燃，表面 {PLC}

0

PLC Code

UL 746A

Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC}

2

PLC Code

UL 746A

UL Recognized, 94V-2 Flame Class Rating / 阻燃等级 (3)

0.76

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating / 阻燃等级 (3)

1.49

mm

UL 94

UL Recognized, 94-5VA Rating (3)

3.4

mm

UL 94

UL Recognized, 94-5VB Rating (3)

2.48

mm

UL 94

CSA (See File for complete listing)

LS88480

File No.

CSA LISTED

Oxygen Index / 极限氧指数 (LOI)

30

%

ASTM D 2863

Drying Temperature / 干燥温度

80 – 90

°C

Drying Time / 干燥时间

3 – 4

hrs

Drying Time (Cumulative) / 干燥时间（累积的）

8

hrs

Maximum Moisture Content / 含湿量

0.04

%

Melt Temperature / 熔体温度

245 – 275

°C

Nozzle Temperature / 注嘴温度

245 – 275

°C

Front – Zone 3 Temperature / 前区3温度

245 – 275

°C

Middle – Zone 2 Temperature / 中区2温度

220 – 265

°C

Rear – Zone 1 Temperature / 后区1温度

220 – 255

°C

Mold Temperature / 模具温度

60 – 80

°C

Back Pressure / 背压

0.3 – 0.7

MPa

Screw Speed / 螺杆速度

40 – 70

rpm

Shot to Cylinder Size / 每次注射量占料筒熔胶总量的***比

30 – 80

%

Vent Depth / 排气孔深度

0.038 – 0.076

mm