整体轧辊是相对于复合轧辊而言的，整体轧辊的辊身外层与心部以及辊颈采用单一材质铸造或锻造而成，辊身外层和辊颈不同的组织、性能通过铸造或锻造工艺以及热处理工艺过程来控制和调整。

The whole roll is compared to the  roll. The outer layer of the whole roll is made of a single material or forging with a single material. The structure and performance of the roll are  and adjusted by the casting or forging process and the heat treatment process.

初轧机、钢坯连轧机、大型型钢和轨梁轧机、热轧板带钢轧机破鳞和轧边机、型钢轧机的轧边机，还有小型型钢、线棒材轧机的粗轧机架等轧机使用的轧辊，大多采用整体铸造方法生产，这类轧辊使用层较厚，孔型较深。

The rolling mill of rolling mill， billet rolling mill， large type steel and rail beam mill， hot rolled strip mill break scale， rolling edge mill， type steel universal mill， and rolling mill used in small steel and wire rod mill are mostly produced by the whole casting method， which is thicker and deeper.

（1）堆焊前需先将轧辊辊身表面的疲劳层或缺陷，尤其是裂纹必须***清除；  

（2）在堆焊时，crane报价，为了防止裂纹的产生，沈阳crane，必须先加工轧辊辊身预热，预热温度根据轧辊辊及堆焊材料而定。

(1) before welding， the fatigue layer or defect of the roller body surface must be first removed，crane哪里有， especially the crack must be thoroughly removed.

(2) in the process of surfacing， in order to prevent cracks， the roller body must be pre heated， and the preheating temperature should be determined according to roll rolls and surfacing materials.