MECHANICAL机械性能

Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min

57

MPa

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min

5

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min

150

%

ASTM D 638

Tensile Modulus, 50 mm/min / 拉伸模量,50 mm/min

2270

MPa

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距

88

MPa

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距

2340

MPa

ASTM D 790

IMPACT

Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C

587

J/m

ASTM D 256

Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C

480

J/m

ASTM D 256

Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C

54

J

ASTM D 3763

Instrumented IMPACT Total Energy, -30°C / 装有测量仪表的落镖冲击Total Energy，-30°C

54

J

ASTM D 3763

THERMAL

HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火

129

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火

112

°C

ASTM D 648

CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动

7.2E-05

1/°C

ASTM E 831

Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50

130

°C

*** 306

Relative Temp Index, Elec / 相对热指数， 电性能

105

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

80

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

105

°C

UL 746B

PHYSICAL

Specific Gravity/比重

1.15

–

ASTM D 792

Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm

0.5 – 0.7

%

SABIC Method

Melt Flow Rate / 熔流率, 260°C/5.0 kgf

19

g/10 min

ASTM D 1238

ELECTRICAL

Hot Wire Ignition {PLC) / 热丝引燃 {PLC)

3

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC} / 高电流电弧引燃，表面{PLC}

1

PLC Code

UL 746A

Comparative Tracking Index (UL) {PLC} / 漏电起痕指数 (UL) {PLC}

2

PLC Code

UL 746A

FLAME CHARACTERISTICS 火焰特性

UL Recognized, 94HB Flame Class Rating (3) / UL认可，94HB 阻燃等级(3)

1.19

mm

UL 94

CSA (See File for complete listing)

LS88480

File No.

CSA LISTED