Density

1.37

g/cm

Melt Volume-Flow Rate (MVR)(360°C/10.0 kg)

150

cm/10min

Molding Shrinkage

Across Flow

0.82

%

Flow

0.79

%

Water Absorption

Saturation, 23°C

2.2

%

Equilibrium, 23°C, 50% RH

0.80

%

Nominal Value

Unit

Test Method

Ball Indentation Hardness

154

MPa

Nominal Value

Unit

Test Method

Tensile Modulus(23°C)

2650

MPa

Tensile Stress(Yield, 23°C)

85.0

MPa

Tensile Strain(Yield, 23°C)

6.8

%

Nominal Value

Unit

Test Method

Charpy Notched Impact Strength

-30°C

7.0

kJ/m

23°C

6.5

kJ/m

Charpy Unnotched Impact Strength

-30°C

No Break

23°C

No Break

Notched Izod Impact Strength

-30°C

7.0

kJ/m

23°C

6.5

kJ/m

Nominal Value

Unit

Test Method

Deflection Temperature Under Load(1.8 MPa, Unannealed)

203

°C

CLTE - Flow

5.2E-5

cm/cm/°C

RTI Elec

1.6 mm

180

°C

3.0 mm

180

°C

RTI Imp

1.6 mm

180

°C

3.0 mm

180

°C

RTI Str

1.6 mm

190

°C

3.0 mm

190

°C

Nominal Value

Unit

Test Method

Surface Resistivity

> 1.0E+15

ohms

Volume Resistivity

> 1.0E+15

ohms·cm

Electric Strength

37

kV/mm

Dielectric Constant

100 Hz

3.90

1 MHz

3.80

Dissipation Factor

100 Hz

1.7E-3

1 MHz

0.014

Comparative Tracking Index

125

V

Nominal Value

Unit

Test Method

Flame Rating

1.6 mm

V-1

3.0 mm

V-0