Elastollan 1180A10 德国巴斯夫TPU 挤出注射成型

　　Elastollan 1180A10热塑性聚氨酯弹性体（聚醚）BASF Corp. Thermoplastic Polyurethanes产品说明：Elastollan 1180A is specifically formulated for extruded profile, sheet and film applications. Elastollan 1180A exhibits excellent abrasion resistance, toughness, transparency, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan 1180A is rated UL-94 HB in vertical flame test for wall thickness of 0.83 mm. Elastollan 1180A also conforms to the FDA food contact section, book 21, section 177.2600. Elastollan 1180A also has NSF Standard 61 "Water Contact Material" certification. Elastollan 1180A is supplied uncolored in diced or pelletized form.

挤出技术:管材和型材:管材和型材大多水平挤压。然而，薄壁管，例如消防水带内衬，一般垂直挤压。有必要提供支撑空气，以防止坍塌的管子。为了协助中空形状稳定性的形状，推荐使用真空。导辊在冷却浴应匹配的形状挤出物。护套:护套电缆，软管等是用十字头进行（见如图。 23），配备有压力或管模头（参见图19）。该内芯 这是要护套必须干燥和无油脂，以避免挤压后和起泡***良好的粘接。

特殊的加工方法:以下特殊方法适用为的Elastollan：共挤出:实现物业组合在一个不同的热塑性塑料处理步骤。粘接材料的原因有是兼容的。相容性的Elastollan醚之间差异酯型。热塑性发泡挤出:为减轻重量，并实现特殊性能。两种方法都适用：?化学膨胀:熔体通过添加扩展的代理与传统挤出机;与泡沫密度0.4和1.0克/立方厘米是可以实现的。?物理膨胀:熔体通过喷射气体的进挤出机。下面的泡沫密度为0.4g /立方厘米是可以实现的。该泡沫的结构是由控制成核剂。

机械加工

焊接:下面焊接技术已被证明是成功的成品和半成品粘合ELASTOLLAN部分：注塑件，主要通过热板粘合，超声波（硬型），高频率或摩擦焊接。对于半成品和型材热板状或摩擦焊接是使用，以及热气焊接。对于薄膜的结果是由实现热合，热冲击焊接或高频 焊接。决定性的焊接强度是：这使得温度下面分解温度足够的流动的Elastollan的，并且压力产生的熔流通和两层的密封。压力也提供了稳定焊接接头的过程中设置时间。 在所有的焊接作业，提供必须的萃取进行气体.

粘接:为了便于接合是推荐使用的Elastollan无等级的润滑油。基于聚氨酯弹性胶已经在证明是成功的中的Elastollan部分粘接。环氧树脂树脂粘合剂用于粘结金属和其他硬质材料。胶粘剂制造商提供适用系统用于此目的。平时的准备工作应该粘接前进行。

表面处理:印刷和绘画是可能的当润滑剂 - 自由的Elastollan等级使用。合适的印刷和绘画系统是由颜料和染料提供制造商。

切削参数:由于出色的韧性和的Elastollan的撕裂强度，加工也不是没有问题的，而在很大程度上取决于硬度材料进行加工。随着用于加工所有的工具ELASTOLLAN，应注意以 确保切削刃正确激化。在加工的Elastollan，excessiv产生的热应避免。因此，永远提供用于通过压缩空气冷却或乳液。