VECTRA? A430

LCP

典型数据

加工方法

注塑

供货形式

粒料

添加剂

阻燃剂

特殊性能

光稳定/耐光的, 阻燃剂

产品

LCP/PTFE, excellent wear & electrical properties at high frequencies
Provides many of the characteristics of A130 with added lubricity.  Suitable for applications requiring excellent wear characteristics.  Excellent electrical properties at high frequencies.  LCP/PTFE blend.   Chemical abbreviation according to *** 1043-1 : LCP Inherently flame retardant FDA compliant version available UL-Listing V-0 in natural and black at 0.43mm thickness per UL 94 flame testing.   Relative-Temperature-Index (RTI) according to  UL 746B: electrical 130°C, mechanical 130°C.  UL = Underwriters Laboratories (USA)

流变性能

Value

单位

测试方法

模塑收缩率, 平行

%

***  294-4, 2577

模塑收缩率, 垂直

0.7

%

***  294-4, 2577

机械性能

Value

单位

测试方法

拉伸模量

7000

MPa

*** 527-1/-2

断裂应力, 5mm/min

150

MPa

*** 527-1/-2

断裂伸长率, 5mm/min

5.8

%

*** 527-1/-2

弯曲模量

7100

MPa

*** 178

弯曲强度

120

MPa

*** 178

Compressive stress at 1% strain

38

MPa

*** 604

简支梁无缺口冲击强度, +23°C

86

kJ/m?

*** 179/1eU

简支梁缺口冲击强度, +23°C

47

kJ/m?

*** 179/1eA

悬臂梁缺口冲击强度, 23°C

34

kJ/m?

*** 180/1A

无缺口悬臂梁冲击强度, 23°C

67

kJ/m?

*** 180/1U

洛氏硬度， M

55

*** 2039-2

热性能

Value

单位

测试方法

熔融温度, 10°C/min

280

°C

*** 11357-1/-3

热变形温度, 1.80 MPa

165

°C

*** 75-1/-2

热变形温度, 0.45 MPa

227

°C

*** 75-1/-2

热变形温度, 8.00 MPa

89

°C

*** 75-1/-2

维卡软化温度, 50°C/h 50N

138

°C

*** 306

燃烧性能

Value

单位

测试方法

厚度为h时的燃烧性

V-0

class

UL 94

电性能

Value

单位

测试方法

相对介电常数., 100Hz

3.3

IEC 62631-2-1

相对介电常数., 1MHz

2.7

IEC 62631-2-1

介质损耗因子, 100Hz

300

E-4

IEC 62631-2-1

介质损耗因子, 1MHz

160

E-4

IEC 62631-2-1

体积电阻率

1E13

Ohm.m

IEC 62631-3-1

表面电阻率

1E15

Ohm

IEC 62631-3-2

介电强度

36

kV/mm

IEC 60243-1

相对漏电起痕指数

PLC 3

PLC

UL 746A

电弧电阻

130

s

Internal

其它性能

Value

单位

测试方法

密度

1500

kg/m?

*** 1183

注塑

Value

单位

干燥温度

150

°C

干燥时间，除湿干燥机

4 - 6

h

加工前水分含量

0.01

%

螺杆切线速度

0.17 - 0.18

m/s

模具温度

80 - 120

°C