G367M不锈钢焊条产品详细说明：

锈钢电焊条

ASpezial

E318-15

≤0.07

1.3

<0.5

19.0

12.0

2.8

>10×C

390

600

30

AW

E318-17

<0.03

0.8

<0.9

19.0

12.0

2.8

>10×C

390

600

30

ATS4

E308H-15

0.05

1.6

0.3

18.5

9.5

350

550

35

C

E310-15

0.13

2.5

1.0

25.0

20.0

350

550

25

CW310-16

E310-16

0.10

2.0

0.5

26.0

21.0

380

570

35

CM

E310-15

0.12

4.5

1.0

25.0

20.0

380

550

30

CR

E310H-15

0.40

2.5

1.0

25.5

21.5

400

600

10

D

E309-15

0.11

0.9

1.0

22.5

11.0

350

550

30

DW

E309-17

0.11

0.8

0.9

22.5

12.5

350

550

30

GESpezial

E316L-15

≤0.04

1.3

0.2

18.5

11.5

2.8

350

580

35

GEW/F(向下立焊)

E316L-16

0.02

0.8

0.7

18.5

11.5

2.6

350

580

30

GEW316L-17

E316L-17

≤0.04

0.8

<0.9

19.0

12.5

2.8

350

580

35

HESpezial

E347-15

≤0.03

1.3

0.5

19.5

10.0

>13×C

390

550

30

HW

E347-17

<0.07

0.8

<0.9

19.5

10.0

>10×C

380

550

30

JESpezial

E308L-15

≤0.04

1.0

0.3

19.5

10.0

350

550

35

JEW308L-17

E308L-17

<0.04

0.8

<0.9

19.5

9.5

350

550

35

X

E307-15

0.10

7.0

0.6

18.5

8.0

0.12

390

620

35

XW

E307-16

0.10

7.0

0.6

18.5

8.0

0.08

390

620

35

13/04

E410NiMo-15

0.04

0.5

<0.4

12.0

4.5

0.5

620

830

15

14K

E410-15

0.06

0.5

<0.4

12.5

1.3

450

650

15

14KSo

E410-15

0.06

0.5

<0.4

12.0

1.1

450

650

20

16/36

E330-15

0.22

1.3

<0.5

18.5

35.0

2.3

320

550

15

17

E430-15

0.06

0.5

0.5

17.0

<0.6

340

530

20

1720

E430-15

0.18

0.40

≤0.5

16.0

0.50

1.10

产品详情

符合：GB T983 E410NiMo-16 
         AWS A5.4 E410NiMo-16 

特性与用途：

1、TS-410NM是钛钙型药皮不锈钢焊条，熔敷金属韧性比TS-410好，用途较广。

2、适用于ASTM CA6NM（JIS SCS6、SCS5）铸铁或相似材料如410、410S和405母材的焊接。

注意事项：

1、使用前焊条须于300～350℃再烘干1小时。

2、应使用不锈钢刷清理焊缝，以免混入铁屑影响品质。

3、尽可能使用较低焊接电流且压低电弧长度，以防止裂纹。

4、焊接前母材预热至100~150℃，焊接后需进行改为595-620℃后热处理。

焊接位置：