Physical Properties	Metric	English	Comments

Specific Gravity	1.20 g/cc	1.20 g/cc	ASTM D792
Density	1.20 g/cc	0.0434 lb/in?	*** 1183
Moisture Absorption	0.0200 %	0.0200 %	Injection Molding
	0.300 %	0.300 %	23°C / 50% RH; *** 62
Water Absorption at Saturation	0.30 %	0.30 %	*** 62-1
Viscosity	30 cP @Load 2.16 kg, Temperature 330 °C	30 cP @Load 4.76 lb, Temperature 626 °F	MVR cc/10 min; *** 1133
Linear Mold Shrinkage, Flow	0.0060 - 0.0090 cm/cm @Thickness 3.20 mm	0.0060 - 0.0090 in/in @Thickness 0.126 in	SABIC method
Melt Flow	33 g/10 min @Load 2.16 kg, Temperature 330 °C	33 g/10 min @Load 4.76 lb, Temperature 626 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	55.0 MPa	7980 psi	50 mm/min; ASTM D638
	60.0 MPa	8700 psi	50 mm/min; *** 527
Tensile Strength, Yield	70.0 MPa	10200 psi	50 mm/min; ASTM D638
	70.0 MPa	10200 psi	50 mm/min; *** 527
Elongation at Break	70 %	70 %	50 mm/min; ASTM D638
	70 %	70 %	50 mm/min; *** 527
Elongation at Yield	6.0 %	6.0 %	50 mm/min; ASTM D638
	6.0 %	6.0 %	50 mm/min; *** 527
Tensile Modulus	2.50 GPa	363 ksi	1 mm/min; *** 527
	2.70 GPa	392 ksi	5 mm/min; ASTM D638
Flexural Strength	80.0 MPa	11600 psi	yield, 2 mm/min; *** 178
	120 MPa	17400 psi	yld, 1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; *** 178
	2.60 GPa	377 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact Notched	97.0 J	71.5 ft-lb	ASTM D256
	55.0 J @Temperature -30.0 °C	40.6 ft-lb @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (***)	9.00 kJ/m?	4.28 ft-lb/in?	80103; *** 180/1A
	9.00 kJ/m? @Temperature -30.0 °C	4.28 ft-lb/in? @Temperature -22.0 °F	80103; *** 180/1A
Izod Impact, Unnotched (***)	NB	NB	80103; *** 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	80103; *** 180/1U
Charpy Impact Unnotched	NB	NB	Edgew 80103 sp=62mm; *** 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	Edgew 80103 sp=62mm; *** 179/1eU
Charpy Impact, Notched	1.10 J/cm?	5.23 ft-lb/in?	Edgew 80103 sp=62mm; *** 179/1eA
	0.900 J/cm? @Temperature -30.0 °C	4.28 ft-lb/in? @Temperature -22.0 °F	Edgew 80103 sp=62mm; *** 179/1eA
Dart Drop, Total Energy	68.0 J	50.2 ft-lb	ASTM D3763

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	175 - 250 V	175 - 250 V	UL 746A
Hot Wire Ignition, HWI	15 - 30 sec @Thickness 1.50 mm	15 - 30 sec @Thickness 0.0591 in	UL 746A
High Amp Arc Ignition, HAI	>= 120 arcs @Thickness 1.50 mm	>= 120 arcs @Thickness 0.0591 in	UL 746A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C	33.3 ?in/in-°F @Temperature -40.0 - 104 °F	ASTM E831
	60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C	33.3 ?in/in-°F @Temperature -40.0 - 104 °F	*** 11359-2
CTE, linear, Transverse to Flow	60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C	33.3 ?in/in-°F @Temperature -40.0 - 104 °F	ASTM E831
	60.0 ?m/m-°C @Temperature -40.0 - 40.0 °C	33.3 ?in/in-°F @Temperature -40.0 - 104 °F	*** 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	166 °C @Thickness 3.20 mm	331 °F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	152 °C	306 °F	Flatw 80104 sp=64mm; *** 75/Af
	156 °C @Thickness 3.20 mm	313 °F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	168 °C	334 °F	Rate B/50; *** 306
	170 °C	338 °F	Rate B/50; ASTM D1525
	170 °C	338 °F	Rate B/120; *** 306
UL RTI, Electrical	150 °C	302 °F	UL 746B
UL RTI, Mechanical with Impact	130 °C	266 °F	UL 746B
UL RTI, Mechanical without Impact	150 °C	302 °F	UL 746B
Flammability, UL94	HB @Thickness >=1.50 mm	HB @Thickness >=0.0591 in	UL 94
Glow Wire Ignition Temperature	875 °C @Thickness 3.00 mm	1610 °F @Thickness 0.118 in	IEC 60695-2-13
Glow Wire Flammability Index	960 °C @Thickness 3.00 mm	1760 °F @Thickness 0.118 in	IEC 60695-2-12

Processing Properties	Metric	English	Comments
Nozzle Temperature	285 - 320 °C	545 - 608 °F
Zone 2	280 - 310 °C	536 - 590 °F
Zone 3	290 - 325 °C	554 - 617 °F
Melt Temperature	290 - 325 °C	554 - 617 °F	Injection Molding
Mold Temperature	95.0 - 130 °C	203 - 266 °F
Drying Temperature	135 °C	275 °F	Injection Molding
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour	Injection Molding
Back Pressure	0.300 - 0.700 MPa	43.5 - 102 psi
Shot Size	40 - 60 %	40 - 60 %
Vent Depth	0.00250 - 0.00800 cm	0.000984 - 0.00315 in
Screw Speed	40 - 90 rpm	40 - 90 rpm

本公司长期销售沙伯基础 PC，ABS，ASA，EVA，PA6，PBT，PE，PBT，PET，PMMA，POM，PS，PP，PU，PES，PEI料等多种牌号

我司产品均可提供详细物性表(英文和中文版)相关资料；可开13%增值税发票；免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料)；如需试料、了解产品相关信息及当日报价，敬请来电、竭诚为您服务！

供应商信息

东莞市樟木头双浩塑胶原料经营部进入首页

东莞市樟木头双浩塑胶原料经营部经销批发的EVA、EBA、EMA、EEA、PPS、EAA、PA6、PA66、TPEE、 TPU、TPV、PC、TPX、COC、PVDF、PTFE、FEP、PP、PE、ABS、POM、PMMA、PPA、氟橡胶、硅胶.***消费者市场，在消费者当中享有较高的地位，目前本公司产品已热销北京，上海，湖南，湖北，福建，浙江，江苏，山东，河北、河南、广西、贵州、辽宁及覆盖整个珠三角地区。超大规模的货物吞吐量亲密融洽了我们与国内外塑胶原料制造商、供应商之间的关系。公司主营业务如下：通用料; 工程塑料，改性塑料：加玻纤、碳纤、滑石粉、矿纤、阻燃改性；增韧耐寒、抗紫外线、抗静电、导电；增强铁氟龙、硅油填充等。欢迎新老客户来电咨询、洽谈，让我们携手共牵，实现双赢，共创美好明天！

点击查看>

企业类型	个体工商户	公司注册地址	东莞市樟木头镇樟罗龙腾花园一期16号铺位
统一社会信用代码	92441900MA51262745	登记机关	东莞市市场监督管理局
法定代表人	余成义	公司成立日期	2017-11-23
营业期限	2017-11-23 至无固定期限	经营范围	销售：塑胶原料、化工原料（不含危险化学品）。

联系方式

余先生

𐂐𐂑𐂒 𐂐𐂒𐂓𐂑 𐂔𐂑𐂔𐂑

东莞市樟木头双浩塑胶原料经营部

电话 𐂔𐂕𐂖𐂗𐂘𐂐𐂑𐂒𐂐𐂒𐂓𐂑𐂔𐂑𐂔𐂑
地址广东东莞樟木头镇塑胶市场四期

产品推荐

免责声明 :
本页面所展现的PPC LEXAN? XHT3143 沙伯基础高流动性紫外线稳定耐温高信息及其他相关推荐信息，均来源于其对应的商铺，信息的真实性、准确性和合法性由该信息的来源商铺所属企业完全负责。推发网对此不承担任何保证责任。
友情提醒 :
建议您在购买相关产品前务必确认供应商资质及产品质量，过低的价格有可能是虚假信息，请谨慎对待，谨防欺诈行为。