VESTAMID庐 LC-GF23 NC is a semi-crystalline, heat- and UV-stabilized compound based on PA 12 from which connectors are preferrably produced by injection molding. The polyamide compound is especially suitable for the automotive and mobility sector.
The semi-crystalline molding compound absorbs only small amounts of water. Components made from VESTAMID庐 LC-GF23 NC therefore have excellent dimensional accuracy with changing ambient humidity and constant general chemical stability.
The semi-crystalline polymer is characterized by its outstanding mechanical and thermal load capacity.
Molding or process-specific deviations from the recommended processing parameters are possible to a certain extent if the cavity or the process requires it.
VESTAMID庐 LC-GF23 NC is delivered as cylindrical-granules in ready-to-process condition, in moisture-tight packaging.
The results presented were generated from a small number of production lots. They are therefore provisional and not yet the result of a statistical analysis.
Pigmentation may affect values.
FOR FURTHER INFORMATION PLEASE CONTACT US AT EVONIK-HP@EVONIK.COM
OR VISIT OUR PRODUCT AT WWW.VESTAMID.COM
| Mechanical properties *** | dry | Unit | Test Standard |
| Tensile Modulus | 5470 | MPa | *** 527 |
| Yield stress | 106 | MPa | *** 527 |
| Yield strain | 4 | % | *** 527 |
| Stress at break | 101 | MPa | *** 527 |
| Strain at break, 蔚B | 7 | % | *** 527 |
| Nominal strain at break, 蔚tB | 6 | % | *** 527 |
| Charpy impact strength, +23掳C | 91 | kJ/m虏 | *** 179/1eU |
| Type of failure | C | - | - |
| Charpy impact strength, -30掳C | 93 | kJ/m虏 | *** 179/1eU |
| Type of failure | C | - | - |
| Charpy impact strength, -40掳C | 97 | kJ/m虏 | *** 179/1eU |
| Type of failure | C | - | - |
| Charpy notched impact strength, +23掳C | 22 | kJ/m虏 | *** 179/1eA |
| Type of failure | C | - | - |
| Charpy notched impact strength, -30掳C | 15 | kJ/m虏 | *** 179/1eA |
| Type of failure | C | - | - |
| Thermal properties | dry | Unit | Test Standard |
| Melting temperature | 178 | 掳C | *** 11357-1/-3 |
| Glass transition temperature | 42 | 掳C | *** 11357-1/-2 |
| Temp. of deflection under load A, 1.80 MPa | 162 | 掳C | *** 75-1/-2 |
| Temp. of deflection under load B, 0.45 MPa | 178 | 掳C | *** 75-1/-2 |
| Vicat softening temperature A, 10 N, 50 K/h | 176 | 掳C | *** 306 |
| Vicat softening temperature B, 50 N, 50 K/h | 172 | 掳C | *** 306 |
| Physical properties | dry | Unit | Test Standard |
| Density | 1180 | kg/m鲁 | *** 1183 |
| Shore D hardness | 79 | - | *** 7619-1 |
| Rheological properties | dry | Unit | Test Standard |
| Melt volume-flow rate, MVR | 31 | cm鲁/10min | *** 1133 |
| Temperature | 275 | 掳C | - |
| Load | 5 | kg | - |
| Molding shrinkage, parallel | 0.3 | % | *** 294-4, 2577 |
| Molding shrinkage, normal | 0.8 | % | *** 294-4, 2577 |
| Mold temperature | 80 | 掳C | - |
| Melt temperature | 260 | 掳C | - |
| Flow length, flow spiral | 463 | mm | Evonik standard |
| Flow front velocity, flow spiral | 950 | mm/s | Evonik standard |
| Flow cross section | 6 x 2 | mm虏 | Evonik standard |
| Mold temperature, flow spiral | 250 | 掳C | Evonik standard |
| Melt temperature, flow spiral | 80 | 掳C | Evonik standard |
| Injection pressure, flow spiral | 1500 | bar | Evonik standard |
| Flow length, flow spiral | 581 | mm | Evonik standard |
| Flow front velocity, flow spiral | 950 | mm/s | Evonik standard |
| Flow cross section | 6 x 2 | mm虏 | Evonik standard |
| Mold temperature, flow spiral | 250 | 掳C | Evonik standard |
| Melt temperature, flow spiral | 80 | 掳C | Evonik standard |
| Injection pressure, flow spiral | 2000 | bar | Evonik standard |
| Polymer analytics | dry | Unit | Test Standard |
| Moisture content | 0.107 | Gew.-% | *** 15512 |