High viscosity, plasticized, impact modified, heat- and light-stabilized polyamide 12 compound
VESTAMID庐 X7293 BK 9.7507 is a plasticized polyamide 12 compound with heat and light stabilizer for the extrusion of flexible tubing and hose, especially for automotive applications according to DIN 73378, (PA 12-HIPHL, Type 1), ***/DIN 7628-1 (PA 12-HIPEHL, Type 1) and SAE J844.
VESTAMID庐 X7293 BK 9.7507 is distinguished by an easy processing as well as by a high impact strength at low temperatures.
Properties of compounds based on Polyamide 12 vary little with changing humidity due to low moisture absorption. Parts made of this semicrystalline material are characterized by exceptional impact strength, low coefficient of friction and good chemical resistance.
VESTAMID庐 X7293 BK 9.7507 is supplied as cylindrical granules, ready for use, in moisture-proof bags.
Inside the original and undamaged packaging, the product has a shelf life of at least 2 years when stored in dry rooms at temperatures not exceeding 30掳C.
For information about processing of VESTAMID庐, please follow the general commendations about 鈥淧rocessing of VESTAMID庐 compounds鈥�.
FOR FURTHER INFORMATION PLEASE CONTACT US AT EVONIK-HP@EVONIK.COM OR VISIT OUR PRODUCT AT WWW.VESTAMID.COM
| Mechanical properties *** | dry / cond | Unit | Test Standard |
| Tensile Modulus | 410 / 400 | MPa | *** 527 |
| Tensile Strength | 26 / 24 | MPa | *** 527 |
| Yield stress | 26 / 24 | MPa | *** 527 |
| Yield strain | 32 / 32 | % | *** 527 |
| Stress at 50% strain | 26 / 24 | MPa | *** 527 |
| Stress at break | 42 / 40 | MPa | *** 527 |
| Nominal strain at break, 蔚tB | 240 / 250 | % | *** 527 |
| Charpy impact strength, +23掳C | N / N | kJ/m虏 | *** 179/1eU |
| Charpy impact strength, 0掳C | N / N | kJ/m虏 | *** 179/1eU |
| Charpy impact strength, -30掳C | N / N | kJ/m虏 | *** 179/1eU |
| Charpy notched impact strength, +23掳C | 120 / 125 | kJ/m虏 | *** 179/1eA |
| Type of failure | P / P | - | - |
| Charpy notched impact strength, -30掳C | 7 / 6 | kJ/m虏 | *** 179/1eA |
| Type of failure | C / C | - | - |
| Flexural modulus, 23掳C | 400 / 390 | MPa | *** 178 |
| Flexural stress at conv. deflection, 23掳C | 14 / 13 | MPa | *** 178 |
| Flexural strain at flexural strength, 23掳C | 9 / 9 | % | *** 178 |
| Flexural stress at break, 23掳C | N / N | MPa | *** 178 |
| Flexural strain at break, 23掳C | N / N | % | *** 178 |
| Thermal properties | dry / cond | Unit | Test Standard |
| Melting temperature | 172 | 掳C | *** 11357-1/-3 |
| Glass transition temperature | 13 | 掳C | *** 11357-1/-2 |
| Temp. of deflection under load A, 1.80 MPa | 45 | 掳C | *** 75-1/-2 |
| Temp. of deflection under load B, 0.45 MPa | 100 | 掳C | *** 75-1/-2 |
| Vicat softening temperature A, 10 N, 50 K/h | 165 | 掳C | *** 306 |
| Vicat softening temperature B, 50 N, 50 K/h | 130 | 掳C | *** 306 |
| Coeff. of linear therm. expansion, 23掳C to 55 掳C, parallel | 180 | E-6/K | *** 11359-1/-2 |
| Coeff. of linear therm. expansion, 23掳C to 55 掳C, normal | 180 | E-6/K | *** 11359-1/-2 |
| Melting Temperature | 172 | 掳C | ASTM D 3418 |
| Physical properties | dry / cond | Unit | Test Standard |
| Water absorption | 1.3 | % | Sim. to *** 62 |
| Humidity absorption | 0.5 | % | Sim. to *** 62 |
| Density | 1020 | kg/m鲁 | *** 1183 |
| Density | 1020 | kg/m鲁 | ASTM D 792 |
| Burning Behav. | dry / cond | Unit | Test Standard |
| Burnin behav. at thickness h | HB | class | IEC 60695-11-10 |
| Thickness tested | 3.2 | mm | - |
| Burning behav. at 1.5 mm nom. thickn. | HB | class | IEC 60695-11-10 |
| Thickness tested | 1.6 | mm | - |
| Electrical properties | dry / cond | Unit | Test Standard |
| Relative permittivity, 50Hz | 13 | - | IEC 62631-2-1 |
| Relative permittivity, 100Hz | 11 / 12 | - | IEC 62631-2-1 |
| Relative permittivity, 1MHz | 4.6 / 3.7 | - | IEC 62631-2-1 |
| Dissipation factor, 50Hz | 1550 | E-4 | IEC 62631-2-1 |
| Dissipation factor, 100Hz | 2000 / 1470 | E-4 | IEC 62631-2-1 |
| Dissipation factor, 1MHz | 1900 / 1450 | E-4 | IEC 62631-2-1 |
| Volume resistivity, 蟻V | 1E10 / 2.7E9 | Ohm*m | IEC 62631-3-1 |
| Surface resistivity, 蟽C, circular electrodes | 1.9E13 | Ohm per square | IEC 62631-3-2 |
| Electric strength, AC, S20/S20 | 37 | kV/mm | IEC 60243-1 |
| Electric strength, AC, S20/P50 | 30 | kV/mm | Sim. to IEC 60243-1 |
| CTI, test solution A, 50 drops value | 600 | - | IEC 60112 |
| Rheological properties | dry / cond | Unit | Test Standard |
| Melt volume-flow rate, MVR | 53 | cm鲁/10min | *** 1133 |
| Temperature | 275 | 掳C | - |
| Load | 5 | kg | - |
| Molding shrinkage, parallel | 0.9 | % | *** 294-4, 2577 |
| Molding shrinkage, normal | 1.2 | % | *** 294-4, 2577 |
| Mold temperature | 60 | 掳C | - |
| Melt temperature | 220 | 掳C | - |