LNP VERTON RVL29 含有45%长玻璃纤维和10%聚四氟乙烯
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, break, 5 mm/min | 231 | MPa | *** 527 | |
| Tensile Strain, break, 5 mm/min | 2.3 | % | *** 527 | |
| Flexural Stress, yield, 2 mm/min | 361 | MPa | *** 178 | |
| Flexural Strain, break, 2 mm/min | 3.2 | % | *** 178 | |
| Flexural Modulus, 2 mm/min | 13600 | MPa | *** 178 | |
| Flexural Strain, break, 2 mm/min, 60掳C | 3.6 | % | *** 178 | |
| Flexural Strain, break, 2 mm/min, 100掳C | 3.2 | % | *** 178 | |
| Flexural Strain, break, 2 mm/min, 150掳C | 3.5 | % | *** 178 | |
| Flexural Strain, break, 2 mm/min, 200掳C | 2.7 | % | *** 178 | |
| Flexural Stress, yield, 2 mm/min, 60掳C | 300 | MPa | *** 178 | |
| Flexural Stress, yield, 2 mm/min, 100掳C | 256 | MPa | *** 178 | |
| Flexural Stress, yield, 2 mm/min, 150掳C | 204 | MPa | *** 178 | |
| Flexural Stress, yield, 2 mm/min, 200掳C | 162 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min, 60掳C | 11700 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min, 100掳C | 10500 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min, 150掳C | 9000 | MPa | *** 178 | |
| Flexural Modulus, 2 mm/min, 200掳C | 8900 | MPa | *** 178 | |
| IMPACT | 1) | |||
| Izod Impact, notched 80*10*3 -40掳C | 28 | kJ/m虏 | *** 180/1A | |
| Izod Impact, unnotched 80*10*4 +23掳C | 82 | kJ/m虏 | *** 180/1U | |
| Izod Impact, unnotched 80*10*4 -40掳C | 74 | kJ/m虏 | *** 180/1U | |
| Izod Impact, notched 80*10*4 +23掳C | 30 | kJ/m虏 | *** 180/1A | |
| THERMAL | 1) | |||
| Specific Heat | 1478 | J/kg-K | ASTM E1269 | |
| CTE, 23掳C to 60掳C, flow | 2.1E-05 | 1/掳C | *** 11359-2 | |
| CTE, 23掳C to 60掳C, xflow | 4.9E-05 | 1/掳C | *** 11359-2 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 258 | 掳C | *** 75/Af | |
| Thermal Conductivity | 0.27 | W/m-K | ASTM D5930 | |
| PHYSICAL | 1) | |||
| Mold Shrinkage, flow, 24 hrs | 3) | 0.13 | % | *** 294 |
| Mold Shrinkage, xflow, 24 hrs | 3) | 0.48 | % | *** 294 |
| Wear Factor Washer | 21 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual | |
| Dynamic COF | 0.39 | - | ASTM D3702 Modified: Manual | |
| Static COF | 0.4 | - | ASTM D3702 Modified: Manual | |
| Density | 1.65 | g/cm鲁 | *** 1183 | |
| Water Absorption, (23掳C/24hrs) | 1.19 | % | *** 62-1 | |
| Moisture Absorption (23掳C / 50% RH) | 0.46 | % | *** 62 | |
| INJECTION MOLDING | 2) | |||
| Drying Temperature | 80 | 掳C | ||
| Drying Time | 4 | Hrs | ||
| Maximum Moisture Content | 0.15-0.25 | % | ||
| Melt Temperature | 290-305 | 掳C | ||
| Front - Zone 3 Temperature | 290-300 | 掳C | ||
| Middle - Zone 2 Temperature | 290-300 | 掳C | ||
| Rear - Zone 1 Temperature | 280-295 | 掳C | ||
| Mold Temperature | 95-110 | 掳C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-60 | rpm |
供应商信息
东莞市聚浩塑化有限公司 进入首页
东莞市聚浩塑化有限公司---位于广东省东莞市樟木头镇塑胶原料市场中心城,是截止到目前在中国大陆塑胶原料、化工原料经销行业中,最齐全、最丰富、***的现货交易商贸市场。聚浩塑化,多年来从事经营批发与代理国内外塑胶原料现货交易以及进口欧美等各国目前在全球塑料、化工行业中众多占据世界***科技研发的种种工程塑料、特种工程塑料的贸易型公司。? 公司秉承“诚信共赢”的经营宗旨, 经营品种 PA6、PA66、PA46、PA6T、PA9T、PA11、PA12、PA610、PA612、POM、PC、PC/ABS、PBT、PBT/PET、PET、TPE、TPEE、TPV、TPU、PPA、PPS、PPO、ASA、ABS、PMMA、LCP、COC、SBS、SPS、SEBS、PEI、PES、PSU、PEEK等全系列工程塑料。 主要经销产品涉及全球各***,如:杜邦(DUPONT)、奇美(Chimei)、美国液氮(LNP)、台湾南亚(NAN YA)、 伊士曼(Eastman)、美国尔特普(RTP)、美国泰科纳(TICONA)、韩国锦湖(KUMHO)、德国巴斯夫(BASF)、德国拜耳(BAYER)、美国陶氏(DOW)、日本三菱(MITSUBISHI)、日本东丽(TORAY)、日本宇部(UBE)、日本宝理(POLY)、瑞士埃姆斯(EMS)、、法国阿托(ATO)、日本出光(IDEMITSU)、日本帝人(TEIJIN)、沙伯基础(SABIC)等。
点击查看>| 企业类型 | 有限责任公司(自然人独资) | 注册资本 | 50.00万人民币 |
| 公司注册地址 | 东莞市樟木头镇先威大道85-1号塑胶商务中心二期9栋32号 | 统一社会信用代码 | 91441900MA4UNCL112 |
| 登记机关 | 东莞市市场监督管理局 | 法定代表人 | 吴双发 |
| 公司成立日期 | 2016-04-07 | 营业期限 | 2016-04-07 至 无固定期限 |
| 经营范围 | 销售:塑胶原料、其他化工产品(不含危险化学品)、高分子材料。(依法须经批准的项目,经相关部门批准后方可开展经营活动)〓 | ||
产品推荐
推荐产品
本页信息为东莞市聚浩塑化有限公司为您提供的"LNP VERTON RVL29 含有45%长玻璃纤维和10%聚四氟乙烯"产品信息,如您想了解更多关于"LNP VERTON RVL29 含有45%长玻璃纤维和10%聚四氟乙烯"价格、型号、厂家请联系厂家,或给厂家留言。 进入店铺
在线留言