Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min

63

MPa

ASTM D 638

Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min

51

MPa

ASTM D 638

Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min

4.7

%

ASTM D 638

Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min

96.3

%

ASTM D 638

Tensile Modulus / 拉伸模量, 5 mm/min

2670

MPa

ASTM D 638

Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span

102

MPa

ASTM D 790

Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span

2660

MPa

ASTM D 790

Tensile Stress, yield / 抗张程度,屈服, 50 mm/min

64

MPa

*** 527

Tensile Stress, break / 抗张程度,断裂, 50 mm/min

53

MPa

*** 527

Tensile Strain, yield / 拉伸伸长,屈服, 50 mm/min

4.7

%

*** 527

Tensile Strain, break / 拉伸伸长,断裂, 50 mm/min

96.8

%

*** 527

Tensile Modulus / 拉伸模量, 1 mm/min

2460

MPa

*** 527

Flexural Stress, yield / 弯曲强度,屈服, 2 mm/min

94

MPa

*** 178

Flexural Modulus / 挠曲模量, 2 mm/min

2360

MPa

*** 178

Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C

600

J/m

ASTM D 256

Izod Impact, notched / 悬臂梁缺口冲击强度, -30°C

N/A

J/m

ASTM D 256

Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C

48

J

ASTM D 3763

Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 +23°C

17

kJ/m?

*** 180/1A

Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 -30°C

12

kJ/m?

*** 180/1A

Charpy（简支梁缺口冲击强度） 23°C, V-notch（V型切口） Edgew 80*10*4 sp=62mm

17

kJ/m?

*** 179/1eA

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50

111

°C

ASTM D 1525

HDT（热变形温度）, 0.45 MPa, 3.2 mm, unannealed （未退火）

105

°C

ASTM D 648

CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）

7.E-05

1/°C

ASTM E 831

CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）

7.E-05

1/°C

ASTM E 831

CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）

7.E-05

1/°C

*** 11359-2

CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）

7.E-05

1/°C

*** 11359-2

Ball Pressure Test, 75°C +/- 2°C

PASS

–

IEC 60695-10-2

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50

112

°C

*** 306

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/120

114

°C

*** 306

HDT（热变形温度）/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

96

°C

*** 75/Af

Relative Temp Index, Elec / 相对热指数， 电性能

80

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

80

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

80

°C

UL 746B

Specific Gravity / 比重

1.16

–

ASTM D 792

Mold Shrinkage on Tensile Bar / 收缩率, flow（流动） (2)

0.5 – 0.7

%

SABIC Method

Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm

0.5 – 0.7

%

SABIC Method

Mold Shrinkage / 收缩率, xflow（横向）, 3.2 mm

0.5 – 0.7

%

SABIC Method

Melt Flow Rate / 熔流率,, 300°C/1.2 kgf

25.2

g/10 min

ASTM D 1238

Density / 密度

1.2

g/cm?

*** 1183

Water Absorption / 吸水率, (23°C/sat)

0.35

%

*** 62

Moisture Absorption / 吸水率, 平衡 (23°C / 50% RH)

0.15

%

*** 62

Melt Volume Rate / 溶化体积流率, MVR at 300°C/1.2 kg

23

cm?/10 min

*** 1133

Dielectric Strength, in oil / 耐电强度，在油中, 1.6 mm

27

kV/mm

ASTM D 149

Volume Resistivity / 体积电阻率

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity ROA / 表面电阻率

>1.E+15

Ohm

IEC 60093

Relative Permittivity / 相对介电常数, 50/60 Hz

3

–

IEC 60250

Relative Permittivity / 相对介电常数, 1 MHz

2.9

–

IEC 60250

Dissipation Factor / 耗散因素, 50/60 Hz

0.03

–

IEC 60250

Dissipation Factor / 耗散因素, 1 MHz

0.01

–

IEC 60250

Comparative Tracking Index / 相比耐漏电起痕指数

200

V

IEC 60112

UL Recognized, 94V-2 Flame Class Rating / 阻燃等级 (3)

0.45

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating / 阻燃等级 (3)

0.8

mm

UL 94

Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at

1

mm

IEC 60695-2-12

Glow Wire Ignitability Temperature / 热灯丝点火温度, 1.0 mm

800

°C

IEC 60695-2-13

Oxygen Index / 极限氧指数 (LOI)

36

%

*** 4589

Drying Temperature / 干燥温度

90

°C

Drying Time / 干燥时间

4

hrs

Maximum Moisture Content / 含湿量

0.02

%

Melt Temperature / 熔体温度

280 – 300

°C

Nozzle Temperature / 注嘴温度

270 – 290

°C

Front – Zone 3 Temperature / 前区3温度

280 – 300

°C

Middle – Zone 2 Temperature / 中区2温度

270 – 290

°C

Rear – Zone 1 Temperature / 后区1温度

260 – 280

°C

Hopper Temperature / 料筒温度

60 – 80

°C

Mold Temperature / 模具温度

90

°C