Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min

57

MPa

ASTM D 638

Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min

110

%

ASTM D 638

Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span

81

MPa

ASTM D 790

Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span

2030

MPa

ASTM D 790

Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C

774

J/m

ASTM D 256

Izod Impact, notched / 悬臂梁缺口冲击强度, -30°C

694

J/m

ASTM D 256

Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C, 6.4mm

694

J/m

ASTM D 256

Instrumented IMPACT Energy @ peak / 仪表控制抗冲击能量 @ 峰值, 23°C

61

J

ASTM D 3763

Instrumented IMPACT Energy @ peak / 仪表控制抗冲击能量 @ 峰值, -30

65

J

ASTM D 3763

HDT（热变形温度）, 0.45 MPa, 6.4 mm, unannealed （未退火）

135

°C

ASTM D 648

HDT（热变形温度）, 1.82 MPa, 6.4 mm, unannealed （未退火）

127

°C

ASTM D 648

CTE（线形膨胀系数）, -40°C to 95°C, flow（流动）

6.48E-05

1/°C

ASTM E 831

Specific Gravity / 比重

1.19

–

ASTM D 792

Water Absorption / 吸水率, 24 hours

0.16

%

ASTM D 570

Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm

0.5 – 0.7

%

SABIC Method

Melt Flow Rate / 熔流率,, 300°C/1.2 kgf

13

g/10 min

ASTM D 1238

Source GMD, last updated:01/04/2000

Drying Temperature / 干燥温度

120

°C

Drying Time / 干燥时间

3 – 4

hrs

Drying Time (Cumulative) / 干燥时间（累积的）

48

hrs

Maximum Moisture Content / 含湿量

0.02

%

Melt Temperature / 熔体温度

295 – 315

°C

Nozzle Temperature / 注嘴温度

290 – 310

°C

Front – Zone 3 Temperature / 前区3温度

295 – 315

°C

Middle – Zone 2 Temperature / 中区2温度

280 – 305

°C

Rear – Zone 1 Temperature / 后区1温度

270 – 295

°C

Mold Temperature / 模具温度

70 – 95

°C

Back Pressure / 背压

0.3 – 0.7

MPa

Screw Speed / 螺杆速度

40 – 70

rpm

Shot to Cylinder Size / 每次注射量占料筒熔胶总量的***比

40 – 60

%

Vent Depth / 排气孔深度

0.025 – 0.076

mm