Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min

62

MPa

ASTM D 638

Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min

67

MPa

ASTM D 638

Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min

6

%

ASTM D 638

Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min

125

%

ASTM D 638

Tensile Modulus / 拉伸模量, 50 mm/min

2270

MPa

ASTM D 638

Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span

101

MPa

ASTM D 790

Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span

2370

MPa

ASTM D 790

Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C

801

J/m

ASTM D 256

Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C

79

J

ASTM D 3763

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50

143

°C

ASTM D 1525

HDT（热变形温度）, 0.45 MPa, 3.2 mm, unannealed （未退火）

137

°C

ASTM D 648

HDT（热变形温度）, 1.82 MPa, 3.2mm, unannealed （未退火）

126

°C

ASTM D 648

CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）

6.84E-05

1/°C

ASTM E 831

CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）

7.38E-05

1/°C

ASTM E 831

Relative Temp Index, Elec / 相对热指数， 电性能

130

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

120

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

130

°C

UL 746B

Specific Gravity / 比重

1.19

–

ASTM D 792

Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm

0.6 – 0.8

%

SABIC Method

Melt Flow Rate / 熔流率,, 300°C/1.2 kgf

13

g/10 min

ASTM D 1238

Arc Resistance, Tungsten / 耐电弧性 {PLC}

7

PLC Code

ASTM D 495

Hot Wire Ignition / 热丝引燃 {PLC)

2

PLC Code

UL 746A

High Voltage Arc Track Rate / 高电压电弧起痕速率 {PLC}

3

PLC Code

UL 746A

High Ampere Arc Ign, surface / 高电流电弧引燃，表面 {PLC}

2

PLC Code

UL 746A

Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC}

3

PLC Code

UL 746A

UL Recognized, 94V-2 Flame Class Rating / 阻燃等级 (3)

0.8

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating / 阻燃等级 (3)

3.04

mm

UL 94

Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at

1

mm

IEC 60695-2-12

Glow Wire Ignitability Temperature / 热灯丝点火温度, 1.0 mm

850

°C

IEC 60695-2-13

UV-light, water exposure/immersion / 紫外线暴露，耐水/浸渍

F1

–

UL 746C

Drying Temperature / 干燥温度

120

°C

Drying Time / 干燥时间

2 – 4

hrs

Maximum Moisture Content / 含湿量

0.02

%

Melt Temperature / 熔体温度

280 – 310

°C

Nozzle Temperature / 注嘴温度

270 – 290

°C

Front – Zone 3 Temperature / 前区3温度

280 – 310

°C

Middle – Zone 2 Temperature / 中区2温度

270 – 290

°C

Rear – Zone 1 Temperature / 后区1温度

260 – 280

°C

Hopper Temperature / 料筒温度

60 – 80

°C

Mold Temperature / 模具温度

80 – 110

°C